Detect items |
Index |
Folding strength under the natural dampish state ( Mpa ) |
> 9 |
Fold strength after be dipped in water for 24 hours Mpa |
> 8.5 |
Drying shrinkage |
≤ 0.06% |
Tensile strength on the vertical plane Mpa |
≥ 0.5 |
Resistance to impact (500g hammer weight , 12mm board thickness) |
Dropping from 1 , 100mm meter , and has no penetrating cracks |
Anti-folding elastic modulus Mpa |
> 3000 |
Density ( T/M3 ) |
1.1-1.4 |
Expansion coefficient ( % ) after being dipped in water for 24 hours |
< 1.5 |
Fire resistance |
A2 level |
Moisture content (%) |
≤ 8% |
Clutching nail force |
1650N |
Heat conductivity factor ( w/m.k ) |
0.19 ( density ) 1200kg/m3 ) |
Surface water resistance |
No change within 96 hours |
Surface alkali fastness |
No change within 48 hours |
Surface washing fastness |
≥ 5000 times |
Surface aging resistance |
No change within 1000 hours |
Contamination resistanT |
< 15% |
Sound insulation value |
36dB ( single board ) |
water absorption bend |
Bend less than 3mm after water absorption |
Water absorption |
20% |
Bond strength in cyclic test under the damp condition N/mm2 |
≥ 0.3 |
Thickness expansion after the cyclic test under the damp condition % |
1.5% |
Outdoor irradiation |
> Has no change, crusting, no spalling within 250 hours |
- 40℃ |
The size and surface do not change after being frozen |
Distortion performance under the wind pressure |
Third level |
Anti seismic within the distortion performance in the plan |
First level |